Material
SLS Nylon PA11-ESD
SLS PA11 ESD is a bio-based, castor-oil nylon with much lower surface resistance than standard PA11. It dissipates static charge from tools, jigs, and housings used around sensitive electronics.
Manufacturing processes
SLS
About
SLS PA11-ESD is a castor-oil-based nylon 11 with an additive that lowers its surface resistance to roughly 10⁴–10⁵ Ω, so static charge dissipates instead of building up, reducing (not eliminating) the risk of static damage.
Depending on the powder, it can be stiffer than standard PA11 and hold its shape under load at a higher temperature, but it is less ductile than the base material.
SLS PA11-ESD is well suited to jigs, fixtures, and housings used in electronics manufacturing.
Technical Details
- Accuracy
- ±0.4% (lower limit of ±0.4 mm)
- Density
- 1.03 g/cm³
- Min. wall thickness
- 0.8 mm
Technical Properties
- Tensile strength
- 65 MPa
- Tensile modulus
- 3150 MPa
- Tensile elongation
- 20 - 31%
- Flexural strength
- 56 MPa
- Flexural modulus
- 1240 - 3050 MPa
- HDT (0.45 MPa)
- 172 - 186°C
- HDT (1.8 MPa)
- 111°C
- Default layer height
- 0.1 mm
- Default infill
- 100%
- Embossing
- min. 0.5 mm
- Engraving
- min. 0.5 mm
- Interlocking parts
- Yes
- Warping risk
- N/A
- Maximum printing dimensions
- 350 × 350 × 350 mm