SLS Nylon PA 2200
PA 2200 is a widely used white nylon 12 grade with a balanced profile of strength, stiffness, and chemical resistance. It is a standard for functional SLS prototypes and rugged, end-use industrial components.
Manufacturing processes
SLS
About
PA 2200 is a widely used nylon 12 grade. It offers a balanced profile of strength, stiffness, and chemical resistance. Under load it softens at roughly 60-95 °C depending on the powder, far below its light-load deflection temperature (about 140-180 °C).
PA 2200 works well for functional prototypes, housings, and parts with movable connections.
Technical Details
- Accuracy
- ±0.3% (lower limit of ±0.3 mm)
- Density
- 0.93 g/cm³
- Min. wall thickness
- 0.8 mm
Technical Properties
- Tensile strength
- 42 - 52 MPa
- Tensile modulus
- 1500 - 1800 MPa
- Tensile elongation
- 4 - 24%
- Flexural strength
- 58 MPa
- Flexural modulus
- 1200 - 1500 MPa
- Default layer height
- 0.1 mm
- Default infill
- 100%
- Embossing
- min. 1 mm
- Engraving
- min. 1 mm
- Interlocking parts
- Yes
- Warping risk
- Moderate
- Maximum printing dimensions
- 250 × 250 × 250 mm