Markforged® Inconel 625
Markforged® Inconel 625 is a nickel-chromium superalloy with high corrosion resistance and strength at high temperatures, suited to high-temperature fixtures and corrosion-resistant fittings.
Manufacturing processes
About
Markforged® Inconel 625 is a nickel-chromium-molybdenum-niobium superalloy that meets the chemical requirements of ASTM B443 and resists chloride corrosion and high temperatures.
As sintered it reaches about 765 MPa tensile strength, 334 MPa yield, and 42% elongation, retains about 558 MPa tensile strength at 600 °C, and is about 96.5% dense. Yield strength is lower than the wrought minimum (414 MPa), and parts are soft (about 7 HRC).
Markforged® Inconel 625 is a good option for high-temperature fixtures, corrosion-resistant fittings, crucibles, and turbine hardware.
Technical Details
- Accuracy
- ±0.5% (lower limit of ±0.2 mm)
- Density
- 8.5 g/cm³
- Min. wall thickness
- 1 mm
Technical Properties
- Tensile strength
- 765 - 827 MPa
- Tensile modulus
- 150000 - 211000 MPa
- Tensile elongation
- 30 - 42%
- Default layer height
- 0.125 mm
- Default infill
- 20%
- Embossing
- min. 1 mm
- Engraving
- min. 1 mm
- Interlocking parts
- Yes
- Warping risk
- High
- Maximum printing dimensions
- 100 × 100 × 100 mm