Material
Glass Fiber ULTEM 1010
Glass fiber ULTEM 1010 is ULTEM 1010 polyetherimide reinforced with glass fiber for added stiffness and dimensional stability, built on a resin with a glass transition of about 215 °C.
Manufacturing processes
FDM
About
Glass fiber ULTEM 1010 is ULTEM 1010 polyetherimide reinforced with glass fiber, which adds stiffness and dimensional stability to a base resin with a glass transition of about 215 °C and a UL 94 V-0 rating at 1.5 mm.
Like unfilled ULTEM 1010, it is brittle and much weaker across the layers than within them.
Glass fiber ULTEM 1010 is a good option for rigid, high-temperature parts such as electrical and aerospace interior components.
Technical Details
- Accuracy
- ±0.3% (lower limit of ±0.2 mm)
- Density
- 1.51 g/cm³
- Min. wall thickness
- 1 mm
Technical Properties
- Tensile strength
- 58 - 145 MPa
- Tensile modulus
- 4300 - 8790 MPa
- Tensile elongation
- 2 - 3%
- Flexural strength
- 53 - 178 MPa
- Flexural modulus
- 4299 - 8560 MPa
- HDT (0.45 MPa)
- 206 - 212°C
- Default layer height
- 0.2 mm
- Default infill
- 20%
- Embossing
- min. 0.5 mm
- Engraving
- min. 0.5 mm
- Interlocking parts
- Yes
- Warping risk
- Yes, for parts over 140mm or parts with thin long structures
- Maximum printing dimensions
- 300 × 300 × 400 mm